Catalyst system for oxidative dehydrogenation, reactor for preparing butadiene including catalyst system, and method of preparing 1,3-butadiene

ABSTRACT

Provided is a catalyst system for oxidative dehydrogenation, a reactor for preparing butadiene including the catalyst system, and a method of preparing 1,3-butadiene. In the catalyst system for oxidative dehydrogenation, a coating catalyst is diluted with a specific dilution filler and a reactor is filled with the diluted catalyst, or a reactor is filled with a catalyst for oxidative dehydrogenation so that the concentration of an active ingredient included in the catalyst gradually increases in the direction from reactants inlet in which reactants are fed into the reactor to products outlet. The catalyst system for oxidative dehydrogenation can efficiently control heat generated inside a reactor, thereby improving conversion rate, selectivity, yield, and long-term stability of a catalyst.

TECHNICAL FIELD

The present invention relates to a catalyst system for oxidativedehydrogenation, a reactor for preparing butadiene including thecatalyst system, and a method of preparing 1,3-butadiene. Morespecifically, the present invention relates to a catalyst system foroxidative dehydrogenation, wherein a coating catalyst having a poroussupport coated with an active ingredient is diluted with a dilutionfiller and a reactor is filled with the diluted catalyst, or a reactoris filled with a catalyst for oxidative dehydrogenation so that theconcentration of an active ingredient included in the catalyst graduallyincreases in the direction from reactants inlet in which reactants arefed into the reactor to products outlet. According to the catalystsystem of the present invention, heat generated inside a reactor can beefficiently controlled, whereby conversion rate, selectivity, and yieldcan be greatly improved and long-term stability of a catalyst can beimproved.

BACKGROUND ART

1,3-butadiene, a major basic product of petroleum fraction, is arepresentative raw material used in preparation of synthetic rubber, andthe price thereof fluctuates rapidly in connection with supply anddemand of the petrochemical industry. Examples of methods of preparing1,3-butadiene include naphtha cracking, direct dehydrogenation of normalbutene, oxidative dehydrogenation of normal butene, and the like.

According to the method of preparing 1,3-butadiene by oxidativedehydrogenation of normal butene, butene and oxygen react in thepresence of a metal oxide catalyst to generate 1,3-butadiene and water.In this case, water generated as a result of the reaction is stable.Thus, the method is thermodynamically very advantageous. In addition,since oxidative dehydrogenation of normal butene is an exothermicreaction unlike direct dehydrogenation, reaction can be performed at alow temperature. Thus, 1,3-butadiene can be obtained in high yield whilereducing energy consumption. In addition, in the case of oxidativedehydrogenation, since an oxidizing agent is added, the generationamount of carbon deposits which shorten catalyst life by poisoning thecatalyst is reduced. Further, since removal of the oxidizing agent iseasy, the method of preparing 1,3-butadiene using oxidativedehydrogenation is very suitable for commercialization.

However, heat generated during oxidative dehydrogenation is accumulatedin a catalyst bed, deteriorating a catalyst, thereby degrading catalystlife, and side reaction is promoted by excess heat, thereby reducingreaction efficiency. As a result, butadiene yield, selectivity forbutadiene, and the conversion rate of butene can be lowered.

To solve these problems, a method of controlling space velocity bycontrolling the amount of gas fed to a reactor has been proposed.However, this method was unsatisfactory in terms of productivity andyield. Thus, development of a system for oxidative dehydrogenation ofbutene that can effectively control heat generated inside a reactorwhile having high productivity is still required.

Prior Art Document

[Patent Document] (Patent Document 1) KR 10-1508776 B1

DISCLOSURE Technical Problem

Therefore, the present invention has been made in view of the aboveproblems, and it is one object of the present invention to provide acatalyst system for oxidative dehydrogenation capable of effectivelycontrolling heat generated inside a reactor to prevent catalystdeterioration, thereby improving conversion rate, selectivity, andyield.

It is another object of the present invention to provide a reactor forpreparing butadiene including the catalyst system for oxidativedehydrogenation and a method of preparing 1,3-butadiene using thereactor.

The above and other objects can be accomplished by the present inventiondescribed below.

Technical Solution

In accordance with one aspect of the present invention, provided is acatalyst system for oxidative dehydrogenation, wherein a reactor isfilled with a catalyst for oxidative dehydrogenation in an n-layerstructure (n being an integer of 2 or more), wherein the catalyst isdiluted and the reactor is filled with the diluted catalyst so that eachlayer of the n-layer structure satisfies Equations 1 and 2 below.

X wt %+Y wt %+Z wt %=100 wt %,   [Equation 1]

wherein X represents a content of AB₂O₄ and is 3 to 30, wherein A is oneor more selected from the group consisting of copper (Cu), radium (Ra),barium (Ba), strontium (Sr), calcium (Ca), beryllium (Be), zinc (Zn),magnesium (Mg), manganese (Mn), cerium (Ce), zirconium (Zr), lanthanum(La), and cobalt (Co) and B is iron (Fe); Y is a content of a poroussupport and is 20 to 97; and Z is a content of one or more dilutionfillers selected from alumina, silica, silicon carbide, zirconia,titania, and cordierite and is 0 to 77.

X _(n) >X _(n−1),  [Equation 2]

wherein, with respect to the direction in which reactants are fed intothe reactor, X_(n) represents X for the n-th layer, and X_(n−1)represents X for the (n−1)th layer.

In accordance with another aspect of the present invention, provided isa catalyst system for oxidative dehydrogenation, wherein a reactor isfilled with a catalyst for oxidative dehydrogenation, wherein thecatalyst is diluted and the reactor is filled with the diluted catalystso as to satisfy Equation 6 below.

X wt %+Y wt %+Z wt %=100 wt %,  [Equation 6]

wherein X is a content of AB₂O₄ and is 5 to 25, wherein A is one or moreselected from the group consisting of copper (Cu), radium (Ra), barium(Ba), strontium (Sr), calcium (Ca), beryllium (Be), zinc (Zn), magnesium(Mg), manganese (Mn), cerium (Ce), zirconium (Zr), lanthanum (La), andcobalt (Co) and B is iron (Fe); Y is a content of a porous support andis 25 to 85; and Z is a content of one or more selected from alumina,silica, silicon carbide, zirconia, titania, and cordierite and is 10 to70.

In accordance with another aspect of the present invention, provided isa reactor for preparing butadiene including the catalyst system foroxidative dehydrogenation.

In accordance with yet another aspect of the present invention, providedis a method of preparing 1,3-butadiene including performing oxidativedehydrogenation using the reactor for preparing butadiene of the presentinvention, wherein the oxidative dehydrogenation is performed whilecontinuously passing reactants containing a C4 compound including normalbutene through the catalyst bed of the reactor.

Advantageous Effects

As apparent from the foregoing, the present invention advantageouslyprovides a catalyst system for oxidative dehydrogenation, wherein acatalyst having a porous support on which an active ingredient isuniformly and firmly coated is diluted in a dilution filler and areactor is filled with the diluted catalyst, or a reactor is filled witha catalyst for oxidative dehydrogenation so that the concentration of anactive ingredient included in the catalyst gradually increases in thedirection from reactants inlet in which reactants are fed into thereactor to products outlet. When the catalyst system according to thepresent invention is used, it is possible to effectively controldistribution of heat generated inside a reactor during oxidativedehydrogenation without adding a separate apparatus or changing theconventional manufacturing facilities, and thus to improve conversionrate, selectivity, and yield. In addition, catalyst deterioration can bereduced, thereby improving long-term stability of a catalyst.

DESCRIPTION OF DRAWINGS

FIG. 1 is a graph showing temperature distribution inside a catalyst bedwhen oxidative dehydrogenation is performed using the catalyst systemaccording to Example 1.

FIG. 2 is a graph showing temperature distribution inside a catalyst bedwhen oxidative dehydrogenation is performed using the catalyst systemaccording to Additional Comparative Example 3.

BEST MODE

Hereinafter, the catalyst system for oxidative dehydrogenation accordingto the present invention will be described in detail.

In the catalyst system for oxidative dehydrogenation according to thepresent invention, a catalyst for oxidative dehydrogenation is dilutedto satisfy Equation 1 below, and a reactor is filled with the dilutedcatalyst.

X wt %+Y wt %+Z wt %=100 wt %,  [Equation 1]

wherein X represents a content of AB₂O₄ and is 3 to 30, wherein A is oneor more selected from the group consisting of copper (Cu), radium (Ra),barium (Ba), strontium (Sr), calcium (Ca), beryllium (Be), zinc (Zn),magnesium (Mg), manganese (Mn), cerium (Ce), zirconium (Zr), lanthanum(La), and cobalt (Co) and B is iron (Fe); Y is a content of a poroussupport and is 20 to 97; and Z is a content of one or more dilutionfillers selected from alumina, silica, silicon carbide, zirconia,titania, and cordierite and is 0 to 77.

X _(n) >X _(n−1),  [Equation 2]

wherein, with respect to the direction in which reactants are fed intothe reactor, X_(n) represents X for the n-th layer, and X_(n−1)represents X for the (n−1)th layer.

According to the present invention, AB₂O₄ is the active ingredient of acatalyst, and the catalyst for oxidative dehydrogenation is a coatingcatalyst having a porous support coated with the active ingredientAB₂O₄.

For example, AB₂O₄ can be a zinc ferrite (ZnFe₂O₄), wherein A is zinc(Zn) and B is iron (Fe). In this case, the catalyst can exhibitexcellent activity in oxidative dehydrogenation of normal butene, andcan have high selectivity for 1,3-butadiene.

For example, AB₂O₄ can have an average particle diameter of 0.1 to 250μm, 10 to 200 μm, 15 to 150 μm, 15 to 100 μm, 15 to 60 μm, or 25 to 60μm. Within this range, coating of the active ingredient on the poroussupport can be easily performed, and the catalyst can have excellentactivity, thereby improving reaction efficiency.

According to the present invention, AB₂O₄ having an average particlediameter within the above range can be selected, for example, using asieving method.

For example, in Equation 1, X is preferably 3 to 30, 3 to 27, 3.5 to 20,3.5 to 18, or 3.5 to 14. Within this range, reaction efficiency can beexcellent, thereby improving yield, selectivity, and conversion rate.

For example, the porous support can have an average particle diameter of3 to 7 mm or 4 to 6 mm. Within this range, reaction efficiency can beexcellent, thereby improving conversion rate and selectivity.

For example, the porous support can have an average pore size of 50 to200 μm or 100 to 150 μm. Within this range, coating of AB₂O₄ powder canbe easy performed and desorption of the powder can be prevented.

According to the present invention, the average particle diameter andaverage pore size of the porous support can be measured, for example,using a method of calculating a surface area and an average pore sizethrough adsorption isotherm of nitrogen by the BET method and the BJH(Barret-Joyner-Halenda) method, respectively, or using a mercuryimpregnation method.

The porous support can have a packing density of 0.8 to 1.5 kg/m³ or 0.9to 1.3 kg/m³. Coating rate is determined based on the packing density.When the porous support has a packing density within this range,separation or desorption of the AB₂O₄ powder can be prevented, and thesupport can be easily coated with the powder. Further, when oxidativedehydrogenation is performed, the conversion rate of butene or1,3-butadiene yield can be increased, and excessive increase in thetemperature inside a catalyst bed can be suppressed, thereby increasingthermal stability.

According to the present invention, packing density is calculated bydividing mass capable of filling a tubular measuring cylinder to 100 ccby a volume value of 100 cc thereof.

The porous support is preferably spherical, hollow, or in the form ofpellets. In this case, reaction efficiency can be excellent, therebyimproving yield, selectivity, and conversion rate.

In the present invention, spherical, pellet, and hollow shapes are notparticularly limited as long as they are within the ordinary range ofthose skilled in the art of porous support technology, and these shapesare clearly distinguished.

For example, the porous support can be one or more selected from thegroup consisting of alumina, silica, titania, zirconia, silicon carbide,and cordierite, and is preferably alumina or silica. In this case,mechanical strength for filling a reactor is satisfied and side reactioncan be reduced.

More preferably, the porous support is alumina. In this case, mechanicalstrength can be ensured, and butadiene yield and selectivity can beprevented from being lowered by side reaction during oxidativedehydrogenation.

For example, in Equation 1, Y can be 20 to 97, 21 to 90, 21 to 86, 30 to86, or 40 to 86. Within this range, catalytic activity and heatgeneration control can be excellent.

The coating catalyst of the present invention can further include anorganic/inorganic binder when necessary. In this case, the binder can beincluded in an amount of 30 parts by weight or less, 0.1 to 20 parts byweight, or 0.1 to 10 parts by weight based on 100 parts by weight ofAB₂O₄. Within this range, the abrasion resistance of the catalyst can beimproved without significantly lowering the efficiency of oxidativedehydrogenation.

For example, the binder can include aluminum-silicate, methylcellulose,hydroxypropyl methylcellulose, or both. When the binder is contained inan appropriate amount, the abrasion resistance of the catalyst can beimproved without significantly lowering the efficiency of oxidativedehydrogenation.

As another example, the coating catalyst of the present invention can bea binder-free catalyst. In this case, since side reaction is not causedby the binder, the conversion rate of normal butene and selectivity forbutadiene can be greatly increased. In addition, since introduction ofsome components is omitted, a process of preparing the catalyst can besimplified, thereby reducing process costs.

According to the present invention, binder-free means that an organic orinorganic binder is omitted when preparing a catalyst and/or that acatalyst is prepared without the binder.

For example, a fixed-bed reactor can be filled with the catalyst foroxidative dehydrogenation according to the present invention in a 2- to8-layer, 3- to 8-layer, 3- to 6-layer, or 3- to 5-layer structure.Within this range, distribution of heat generated inside the reactor canbe effectively controlled without significantly increasing processcosts. Thus, when butadiene is prepared, conversion rate, selectivity,and yield can be greatly improved, and long-term stability of thecatalyst can be improved.

For example, the catalyst system of the present invention satisfiesEquation 3 below. In this case, excessive heat generation in thecatalyst bed can be effectively prevented during reaction. As a result,when butadiene is prepared, conversion rate, selectivity, yield, andlong-term stability of the catalyst can be improved.

(X _(n) −X _(n−1))≥2,  [Equation 3]

wherein X_(n) represents X for the n-th layer, and X_(n−1) represents Xfor the (n−1)th layer.

According to the present invention, at least one of the n layers canhave a Z value greater than 0. When the coating catalyst is mixed with adilution filler and a reactor is filled with the coating catalyst sothat the concentration of the catalyst is gradually decreased, heatgeneration control can be effectively performed during reaction, therebyimproving reaction efficiency.

According to the present invention, the dilution filler can be, forexample, one or more selected from alumina, silica, silicon carbide,zirconia, titania, and cordierite, and is preferably one or moreselected from alumina and silica. In this case, it is possible tosuppress generation of excessive reaction heat while minimizing sidereaction, thereby greatly improving the efficiency of oxidativedehydrogenation.

The catalyst system of the present invention satisfies Equation 4 belowwhen at least one layer has a Z value other than 0. In this case,excessive temperature increase of the catalyst bed due to excessive heatmay be suppressed, and thus productivity such as conversion rate,selectivity, and yield can be greatly improved when butadiene isprepared.

(Y _(n−1) −Y _(n))≥15,[Equation 4]

wherein Y_(n) represents Y for the n-th layer, and Y_(n−1) represents Yfor the (n−1)th layer.

In addition, the catalyst system of the present invention satisfiesEquation 5 below. In this case, heat generation due to oxidativedehydrogenation can be effectively controlled so that the activity orstability of the catalyst can be continuously maintained high andreaction efficiency can be improved.

(Z _(n−1) −Z _(n))≥20,  [Equation 5]

wherein Z_(n) represents Z for the n-th layer, and Z_(n−1) represents Zfor the (n−1)th layer.

As another example, in the catalyst system for oxidative dehydrogenationaccording to the present invention, a reactor is filled with thecatalyst for oxidative dehydrogenation in an n-layer structure (n beingan integer of 2 or more). In this case, the catalyst is diluted and thereactor is filled with the diluted catalyst so that each layer satisfiesEquations 1 and 2. In addition, the porous support has a packing densityof 0.8 to 1.5 kg/m³ or 0.9 to 1.2 kg/m³. In this case, separation orpeeling of AB₂O₄ powder from the porous support can be prevented, andthe support can be uniformly and firmly coated with the catalyst. Inaddition, heat generation inside the catalyst bed during oxidativedehydrogenation can be effectively controlled, and side reaction can besuppressed, thereby improving the conversion rate of butene, butadieneyield, and selectivity.

As a specific example, in the catalyst system for oxidativedehydrogenation according to the present invention, a reactor is filledwith the catalyst for oxidative dehydrogenation in a three-layerstructure. In this case, the catalyst is diluted and the reactor isfilled with the diluted catalyst so that each layer satisfies Equations1 and 2 below. With respect to the direction in which reactants are fedinto the reactor, in the case of the first layer, X is 3.5 to 7; Y is21.5 to 43; and Z is 50 to 75, in the case of the second layer, X is 7to 10.5; Y is 43 to 64.5; and Z is 25 to 50, and in the case of thethird layer, X is 13 to 18; Y is 82 to 87; and Z is 0 to 5. In thiscase, excessive temperature rise inside the catalyst bed can beeffectively suppressed. Consequently, compared to the conventionalcatalyst system, the conversion rate of butene and selectivity for1,3-butadiene can be improved.

X wt %+Y wt %+Z wt %=100 wt %,  [Equation 1]

wherein X is a content of zinc ferrite powder wherein A is Zn and B isFe, Y is a content of a porous support, and Z is a content of one ormore dilution fillers selected from alumina, silica, silicon carbide,and zirconia, wherein the porous support is alumina having a packingdensity of 0.8 to 1.5 kg/m³.

X _(n) >X _(n−1),  [Equation 2]

wherein, with respect to the direction in which reactants are fed intothe reactor, X_(n) represents X for the n-th layer, and X_(n−1)represents X for the (n−1)th layer, wherein n is the total number oflayers and is 3.

As a preferred example, in the first layer, X is 3 to 4.5; Y is 20 to35; and Z is 60.5 to 77, in the second layer, X is 5 to 8; Y is 40 to50; and Z is 45 to 55, and in the third layer, X is 10 to 16; Y is 60 to90; and Z is 0 to 30. In this case, excessive temperature rise insidethe catalyst bed can be effectively suppressed. When oxidativedehydrogenation is performed using the catalyst system, side reactioncan be suppressed, and the conversion rate of butene, selectivity forbutadiene, and yield can be improved.

In addition, as another example, in the catalyst system of the presentinvention, the catalyst for oxidative dehydrogenation is diluted and areactor is filled with the catalyst so as to satisfy Equation 6 below.

X wt %+Y wt %+Z wt %=100 wt %,  [Equation 6]

wherein X is a content of AB₂O₄ and is 5 to 25, wherein A is one or moreselected from the group consisting of copper (Cu), radium (Ra), barium(Ba), strontium (Sr), calcium (Ca), beryllium (Be), zinc (Zn), magnesium(Mg), manganese (Mn), cerium (Ce), zirconium (Zr), lanthanum (La), andcobalt (Co) and B is iron (Fe); Y is a content of a porous support andis 25 to 85; and Z is a content of one or more dilution fillers selectedfrom alumina, silica, silicon carbide, zirconia, titania, and cordieriteand is 10 to 70.

Hereinafter, a catalyst system for oxidative dehydrogenation accordingto another embodiment of the present invention, wherein the catalyst isdiluted and a reactor for oxidative dehydrogenation is filled with thediluted catalyst so as to satisfy Equation 6, will be described. Inexplaining the system, the overlapping description with the incrementaldilution filling system of the above-mentioned catalyst for oxidativedehydrogenation will be omitted.

In Equation 6, X is preferably 5 to 25, 7 to 20, 7 to 18, 7 to 14, 7 to13.5, or 7 to 11. Within this range, reaction efficiency can beexcellent, thereby improving yield, selectivity, and conversion rate.

In Equation 6, Y can be, for example, 25 to 85, 35 to 80, 36 to 75, 36.5to 70, 36.5 to 60, or 40 to 50. Within this range, catalytic activityand catalyst stability can be maintained high, and the productivity ofbutadiene can be increased.

In Equation 6, Z can be, for example, 10 to 70, 20 to 70, or 40 to 60.Within this range, excessive heat generation due to oxidativedehydrogenation can be effectively suppressed, thereby improvingcatalyst stability and reaction efficiency.

As a preferred example, the porous support can have a packing density of0.8 to 1.5 kg/m³ or 0.9 to 1.2 kg/m³. Within this range, the mechanicalstrength of the coating catalyst can be excellent, and separation orpeeling of AB₂O₄ powder from the porous support can be prevented. Inaddition, heat generation in the catalyst bed during oxidativedehydrogenation can be effectively suppressed, and butadiene yield andselectivity for butadiene can be improved.

The catalyst system can be an oxidative-dehydrogenation catalyst systemfor preparation of 1,3-butadiene.

In addition, the present invention provides a reactor for preparingbutadiene including the catalyst system and a method of preparing1,3-butadiene using the reactor.

For example, the method of preparing 1,3-butadiene according to thepresent invention includes i) filling a reactor with the catalyst foroxidative dehydrogenation as a fixed bed; and ii) performing oxidativedehydrogenation while continuously passing reactants containing a C4compound including normal butene through the catalyst bed of the reactorfilled with the catalyst, wherein the reactor in step i) is a fixed-bedreactor filled with the catalyst for oxidative dehydrogenation in ann-layer structure (n being an integer of 2 or more) in a progressivedilution manner, wherein each stage of the n-stage structure satisfiesEquations 1 and 2.

As another example, the method of preparing 1,3-butadiene according tothe present invention includes i) filling a reactor with the catalystfor oxidative dehydrogenation as a fixed bed; and ii) performingoxidative dehydrogenation while continuously passing reactantscontaining a C4 compound including normal butene through the catalystbed of the reactor filled with the catalyst, wherein the reactor in stepi) is a fixed-bed reactor, wherein the catalyst for oxidativedehydrogenation is diluted and the fixed-bed reactor is filled with thediluted catalyst so as to satisfy Equation 6.

When a specific catalyst is diluted and a reactor is filled with thediluted catalyst, or a reactor is filled with a specific catalyst in aprogressive dilution manner, and then oxidative dehydrogenation isperformed, heat generation inside the reactor can be effectivelycontrolled. In particular, when a fixed-bed reactor is filled with aspecific catalyst for oxidative dehydrogenation in a progressivedilution manner, heat generation control effect can be maximized,allowing catalytic activity and catalyst stability to remain high over along period of time. In addition, the conversion rate of butene,selectivity for butadiene, and yield can be greatly improved.

The C4 compound can include, for example, one or more normal buteneselected from 2-butene (trans-2-butene, cis-2-butene) and 1-butene, andcan optionally further include normal butane or C4 raffinate-3.

For example, the reactants can further include one or more selected fromair, nitrogen, steam, and carbon dioxide, and preferably furtherincludes nitrogen and steam.

As a specific example, the reactants can include a C4 compound, oxygen,steam, and nitrogen in a molar ratio of 1:0.1 to 1.5:1 to 15:0.5 to 10or 1:0.5 to 1.2:5 to 12:0.5 to 5. In addition, the method of preparingbutadiene according to the present invention shows excellent reactionefficiency and little generation of wastewater even when steam is usedin a small amount (e.g., 1 to 10 mol or 5 to 10 mol based on 1 mol ofthe C4 compound). Ultimately, the method provides the effect of reducingwastewater treatment cost and the effect of reducing energy consumed inthe process.

For example, the oxidative dehydrogenation reaction can be performed ata reaction temperature of 250 to 500° C., 300 to 450° C., 320 to 400°C., 330 to 380° C., or 350 to 370° C. Within this range, reactionefficiency can be excellent without greatly increasing energy cost,thereby increasing the productivity of 1,3-butadiene.

In addition, in oxidative dehydrogenation, the ΔT value calculated byEquation 7 below can be 105° C. or less, 104° C. or less, 90° C. orless, 80° C. or less, 70° C. or less, 60° C. or less, 50° C. or less,40° C. or less, 20 to 70° C., or 20 to 45° C.

ΔT(° C.)=reaction temperature−the maximum temperature inside a catalystbed  [Equation 7]

According to the present invention, the maximum temperature inside thecatalyst bed means the part of the catalyst bed with the highesttemperature during reaction.

In addition, the maximum temperature inside the catalyst bed can bemeasured, for example, by connecting a thermocouple (TC) to a transferdevice and then performing scanning while moving the thermocouple fromthe top of the reactor to the bottom of the reactor at constantvelocity.

For example, oxidative dehydrogenation can be performed at a gas hourlyspace velocity (GHSV) of 50 to 2,000 h⁻¹, 50 to 1,500 h⁻¹, or 50 to1,000 h⁻¹ based on normal butene. Within this range, reaction efficiencycan be excellent, thereby improving conversion rate, selectivity, andyield.

In the present invention, the reactor is not particularly limited aslong as the reactor includes the catalyst system for oxidativedehydrogenation, but can be, for example, a multi-tube reactor or aplate reactor.

Hereinafter, the present invention will be described in more detail withreference to the following preferred examples. However, these examplesare provided for illustrative purposes only and should not be construedas limiting the scope and spirit of the present invention. In addition,it will be apparent to those skilled in the art that various changes andmodifications can be made without departing from the spirit and scope ofthe present invention, and such changes and modifications are alsowithin the scope of the appended claims.

PREPARATION EXAMPLE

1. Preparation of ZnFe₂O₄ Powder

2 L of aqueous ammonia adjusted to have a pH of 8 was prepared. In aseparate container, a metal precursor solution containing 2 L ofdistilled water, 288.456 g of zinc chloride (ZnCl₂), and 1132.219 g ofiron chloride (FeCl₃) was prepared. The prepared metal precursorsolution was added dropwise to the prepared aqueous ammonia, and at thesame time, 9 wt % aqueous ammonia was added thereto to adjust the pH to8. To obtain a sample having a uniform composition, all of the metalprecursor solution was added dropwise with stirring for 1 hour using anagitator, aged for 1 hour, and then the solution including precipitatewas washed with 4 L of distilled water and the precipitate was separatedby filtration. The separated precipitate was dried for 16 hours, andthen burned at 650° C. to obtain ZnFe₂O₄ powder. The obtained powder waspulverized, and then powder having a size of 45 μm or less was selectedusing a sieving method.

2. Preparation of Coating Catalyst

ZnFe₂O₄ powder quantified so that ZnFe₂O₄ has a ratio of 14 wt % or 27wt % based on 100 wt % in total of ZnFe₂O₄ and alumina balls wasdispersed in distilled water to prepare a catalyst slurry having aconcentration of 10 to 30 wt %. Alumina balls having a packing densityof 0.9 to 1.2 kg/m³ were added to a rotary chamber under a vacuumatmosphere. Then, the catalyst slurry was coated on the alumina ballshaving an average particle diameter of 5 mm by spraying the catalystslurry while rotating the rotary chamber at about 30 to 50 rpm. Whencoating was performed, the rotary chamber was set to a temperature of 50to 80° C. After the coating process was completed, a coating catalystwas prepared by drying the catalyst slurry-coated alumina balls in anoven set to 90 to 120° C. so that distilled water was evaporated.

EXAMPLES Example 1

The coating catalyst having ZnFe₂O₄ in an amount of 14 wt % was mixedwith alumina as a dilution filler as shown in Table 1, and a tubularreactor was filled with the catalyst in a three-layer structure and in agradual dilution manner. Then, the conversion rate of butene,selectivity for 1,3-butadiene, 1,3-butadiene yield, and selectivity forCO_(x) were measured.

The C4 compound containing trans-2-butene and cis-2-butene, oxygen,steam, and nitrogen as reactants were mixed in a molar ratio of 1:1:8:1.At this time, the amount of each of the C4 compound, oxygen, andnitrogen was controlled using a mass flow controller, and the injectionrate of steam was controlled using a liquid pump. The feed rate ofreactants was set so that a gas hourly space velocity (GHSV) was 66 h⁻¹based on normal butene in the C4 compound. The reaction was performed atthe reaction temperature shown in Table 1 below.

TABLE 1 GHSV/mole ratio of butene:oxygen:steam:nitrogen = 66h⁻¹/1:1:8:1, 355° C. X [content of Y [content of Z [content of ZnFe₂O₄,porous support, dilution filler, Classification wt %] wt % ] wt % ]Third layer 14 86 0 Second layer 10.5 64.5 25 First layer 7 43 50 * Intable 1, each of X, Y, and Z is based on 100 wt % of the total amountthereof.

Example 2

A reactor was filled with the catalyst composition in a gradual dilutionmanner in a three-layer structure as shown in Table 2 below. Then,reaction was performed under the same conditions and in the same manneras in Example 1, except that the reaction was performed at thetemperature specified in Table 2 below.

TABLE 2 GHSV/mole ratio of butene:oxygen:steam:nitrogen = 66h⁻¹/1:1:8:1, 360° C. X [content of Y [content of Z [content of ZnFe₂O₄,porous support, dilution filler, Classification wt %] wt % ] wt % ]Third layer 14 86 0 Second layer 7 43 50 First layer 3.5 21.5 75 * InTable 2, each of X, Y, and Z is based on 100 wt % of the total amountthereof.

Example 3

The coating catalyst containing ZnFe₂O₄ in an amount of 14 wt % wasdiluted by mixing with a dilution filler as shown in Table 3 and atubular reactor was filled with the diluted catalyst. Then, reaction wasperformed under the same conditions and in the same manner as in Example1, except that reaction temperature was set to 365° C.

Example 4

The coating catalyst containing ZnFe₂O₄ in an amount of 27 wt % wasdiluted by mixing with a dilution filler as shown in Table 3 and atubular reactor was filled with the diluted catalyst. Then, reaction wasperformed under the same conditions and in the same manner as in Example1, except that reaction temperature was set to 340° C.

TABLE 3 GHSV/mole ratio of butene:oxygen:steam:nitrogen = 66 h⁻¹/1:1:8:1X [content Y [content Z [content Reaction of of porous of dilutiontemperature ZnFe₂O₄, support, filler, Classification ( ° C.) wt % ] wt %] wt % ] Example 3 365 7 43 50 Example 4 340 13.5 36.5 50 * In Table 3,each of X, Y, and Z is based on 100 wt % of the total amount thereof.

Comparative Example 1

ZnFe₂O₄ powder prepared in the same manner as in Preparation Exampleswas kneaded with distilled water and an alcohol and thenextrusion-molded to obtain pellets having a diameter of 2 mm and alength of 2 mm, followed by drying at 90° C. for 4 hours to obtain acatalyst in the form of pellets. 6 volume % of the prepared catalyst wasmixed with 94 volume % of alumina balls, and the mixture was loaded intoa reactor. Then, reaction was performed under the same conditions and inthe same manner as in Example 1, except that reaction temperature wasset to 365° C.

Comparative Example 2

ZnFe₂O₄ powder prepared in the same manner as in Preparation Exampleswas kneaded with distilled water and an alcohol and thenextrusion-molded to obtain pellets having a diameter of 2 mm and alength of 2 mm, followed by drying at 90° C. for 4 hours to obtain acatalyst in the form of pellets. A reactor was filled with the preparedcatalyst in a gradual dilution manner as shown in Table 4. Then,reaction was performed under the same conditions and in the same manneras in Example 1, except that reaction temperature was set to 375° C.

TABLE 4 GHSV/mole ratio of butene:oxygen:steam:nitrogen = 66h⁻¹/1:1:8:1,365° C. X [content of Y [content of Z [content of ZnFe₂O₄, poroussupport, dilution filler, Classification wt %] wt % ] wt % ] Third layer9 — 91 Second layer 6 — 94 First layer 3 — 97 * In Table 4, each of Xand Z is based on 100 wt % of the total amount thereof.

Comparative Example 3

A tubular reactor was filled with the coating catalyst containingZnFe₂O₄ in an amount of 14 wt %. In this case, addition of a dilutionfiller was omitted. Then, reaction was performed under the sameconditions and in the same manner as in Example 3, except that reactiontemperature was set to 343° C.

Comparative Example 4

A tubular reactor was filled with the coating catalyst containingZnFe₂O₄ in an amount of 27 wt %. In this case, addition of a dilutionfiller was omitted. Then, reaction was performed under the sameconditions and in the same manner as in Example 4, except that reactiontemperature was set to 325° C.

TEST EXAMPLE

The products according to Examples and Comparative Examples wereanalyzed using gas chromatography. The conversion rate of butene,selectivity for 1,3-butadiene, 1,3-butadiene yield, selectivity for COxwere calculated according to Equations 8, 9, and 10 below, respectively.The results are shown in Tables 5 and 6.

In addition, when oxidative dehydrogenation was performed using thecatalyst systems according to Examples and Comparative Examples, themaximum temperature inside a catalyst bed was analyzed while moving athermocouple in a thermo-well at the center of a reactor from the inletof the reactor to the outlet of the reactor at a constant velocity of 4mm per second.

Conversion rate (%)=[(Number of moles of butene reacted)/(Number ofmoles of butene supplied)]×100  [Equation 8]

Selectivity (%)=[(Number of moles of 1,3-butadiene or CO_(x)generated)/(Number of moles of butene reacted)]×100  [Equation 9]

Yield (%)=[(Number of moles of 1,3-butadiene generated)/(Number of molesof butene supplied)]×100  [Equation 10]

TABLE 5 Conversion Selectivity for Yield of 1.3- Hot rate of1.3-butadiene butadiene Selectivity for spot ΔT butene (%) (%) yield (%)CO_(x) (%) (° C.) (° C.) Example 1 89.8 88.8 79.7 9.8 400 65 Example 291.2 91.7 83.6 7.1 397 37 Comparative 79.6 89.3 71.1 9.1 400 35 Example1 Comparative 83.9 88.4 74.2 10.2 415 40 Example 2 ΔT (° C.): Differencebetween the maximum temperature inside a catalyst bed and the reactiontemperature set during reaction

As shown in Table 5, compared with Comparative Examples 1 and 2, in thecase of Examples 1 and 2 using the catalyst system according to thepresent invention, although oxidative dehydrogenation was performed at arelatively low reaction temperature, it was confirmed that theconversion rate of butene, selectivity for 1,3-butadiene, and1,3-butadiene yield were excellent. In particular, when the catalystsystem according to Example 2 was used, the efficiency and activity ofoxidative dehydrogenation were excellent. In addition, considering thatthe difference between the maximum temperature inside a catalyst bed andthe reaction temperature was small, it was confirmed that heat generatedinside a reactor was effectively controlled.

On the other hand, in the case of the catalyst system according toComparative Example 1, wherein the catalyst in the form of pelletsprepared using ZnFe₂O₄ powder was diluted by mixing a dilution fillerand a reactor was filled with the diluted catalyst, although reactionwas performed at a relatively high reaction temperature, it wasconfirmed that reaction activity was significantly lower than in thecases of Examples. In addition, in the case of Comparative Example 2,although the catalyst in the form of pellets prepared using ZnFe₂O₄powder was diluted by mixing with a dilution filler and a reactor wasfilled with the diluted catalyst in a gradual dilution manner, it wasconfirmed that reaction activity was lower than in Examples.

From the above results, it can be seen that, when the catalyst system,in which a catalyst having a porous support on which ZnFe₂O₄ is coatedin a predetermined ratio is diluted with a dilution filler and a reactoris filled with the diluted catalyst in a gradual dilution manner, isused to perform oxidative dehydrogenation, the activity of oxidativedehydrogenation is greatly improved. In addition, it can be judged thatthis is because heat generation inside the reactor is controlled by thenovel catalyst system according to the present invention, therebyproviding a reaction system with a stable temperature gradient. Inaddition, from the results of Examples 1 and 2, it can be seen that,when the reactor is filled with the coating catalyst in a gradualdilution manner, dilution ratio affects reaction activity.

TABLE 6 Conversion Selectivity for Yield of 1.3- Hot rate of1.3-butadiene butadiene Selectivity for spot ΔT butene (%) (%) (%)CO_(x) (%) (° C.) (° C.) Example 3 90.4 89.0 80.5 9.8 453 88 Comparative88.3 88.5 78.1 10.1 443 100 Example 3 Example 4 86.1 85.8 73.9 11.3 444104 Comparative 82.7 86.6 71.6 12.0 471 146 Example 4 ΔT (° C.):Difference between the maximum temperature inside a catalyst bed and thereaction temperature set during reaction

As shown in Table 6, in the case of the catalyst systems (Examples 3 and4) in which the coating catalyst is homogeneously diluted with adilution filler, compared with the systems of Comparative Examples 3 and4 in which the same coating catalyst was used, but the coating catalystwas not diluted, it was confirmed that the conversion rate of butene,selectivity for 1,3-butadiene, and 1,3-butadiene yield were excellent,and selectivity for COx as a side reaction product and the maximumtemperature inside a catalyst bed were significantly decreased. Inaddition, it was confirmed that this improvement effect was even betterwhen a coating catalyst having a coating ratio of 14 wt % was used.

On the other hand, compared with Example 3, in the case of ComparativeExample 3 in which the same concentration of the coating catalyst wasused as in Example 3, even though reaction temperature was set to be aslow as 22° C., it was confirmed that the maximum temperature inside acatalyst bed was higher by 10° C., and reaction activity wassignificantly decreased. In the case of Comparative Example 4, althoughthe maximum temperature inside a catalyst bed was the highest, it wasconfirmed that reaction activity was significantly decreased.

ADDITIONAL EXAMPLES AND COMPARATIVE EXAMPLES Additional Example 1

Reaction was performed under the same conditions and in the same manneras in Example 1, except that silicon carbide was used as a dilutionfiller.

Additional Example 2

Reaction was performed under the same conditions and in the same manneras in Example 1, except that zirconia was used as a dilution filler.

Additional Comparative Example 1

Reaction was performed under the same conditions and in the same manneras in Example 1, except that, when a coating catalyst was prepared,alumina balls having a packing density of 0.5 kg/m³ were used.

Additional Comparative Example 2

Reaction was performed under the same conditions and in the same manneras in Example 1, except that, when a coating catalyst was prepared,alumina balls having a packing density of 2.0 kg/m³ were used.

Additional Comparative Example 3

ZnFe₂O₄ powder prepared in the same manner as in Preparation Exampleswas kneaded with distilled water and an alcohol and thenextrusion-molded to obtain pellets having a diameter of 5 mm and alength of 5 mm, followed by drying at 90° C. for 4 hours to obtain acatalyst in the form of pellets. A reactor was filled with the preparedcatalyst. In this case, addition of a dilution filler was omitted. Then,reaction was performed under the same conditions and in the same manneras in Example 1, except that reaction temperature was set to 291° C.

The products prepared according to the Additional Examples andAdditional Comparative Examples were analyzed in the same manner asdescribed above, and the results are shown in Table 7.

TABLE 7 Maximum Selectivity Yield of temperature Conversion for 1.3-1.3- inside rate of butadiene butadiene Selectivity catalyst bed ΔTbutene (%) (%) (%) for CO_(x) (%) (° C.) (° C.) Additional 89.2 87.478.0 10.5 401 46 Example 1 Additional 86.7 87.5 75.9 11.1 407 52 Example2 Additional 57.2 91.5 52.3 6.9 407 52 Comparative Example 1 Additional80.1 87.0 69.7 11.0 419 64 Comparative Example 2 Additional 79.4 83.966.6 13.7 474 183 Comparative Example 3 ΔT (° C.) : Difference betweenthe maximum temperature inside a catalyst bed and the reactiontemperature set during reaction

As shown in Table 7, in the case of Examples 1 and 2 in which siliconcarbide and zirconia were used as the dilution filler, respectively, themaximum temperature inside a catalyst bed was equal to or lower thanthat of Comparative Examples 1 and 2, and the conversion rate of butene,selectivity for 1,3-butadiene, and 1,3-butadiene yield were excellent.

In addition, when alumina having a packing density outside the range ofthe present invention was used as the porous support, it was confirmedthat the effect of suppressing overheating of the catalyst bed wasinsufficient even though the catalyst was diluted and supplied tosatisfy Equations 1 and 2, and that the conversion rate of butene andbutadiene yield were significantly reduced. In particular, when thepacking density was less than the lower limit of the present invention(Additional Comparative Example 1), it was confirmed that the conversionrate of butene and butadiene yield were significantly reduced.

In addition, when mixing of the porous support and the dilution fillerwas omitted, as shown in Table 7, it was confirmed that the temperatureinside the catalyst bed was considerably high because heat generationwas not effectively controlled, and selectivity for COx as a sidereaction product was considerably increased. The lifespan of thecatalyst is expected to be considerably short.

FIG. 1 is a graph showing the temperature distribution of the catalystbed when oxidative dehydrogenation is performed using the catalystsystem according to Example 1, and FIG. 2 is a graph showing thetemperature distribution of the catalyst bed when oxidativedehydrogenation is performed using the catalyst system according toAdditional Comparative Example 3 (conventional technology).

Referring to these results, when the catalyst system according to thepresent invention was used, heat generation was effectively controlled,and thus the temperature inside the catalyst bed was kept relativelystable. On the other hand, when the catalyst system of AdditionalComparative Example 3 was used, it was confirmed that the temperatureinside the catalyst bed was drastically increased at the beginning ofreaction, and thereafter was drastically decreased.

According to the results of the experiments, when the catalyst systemaccording to the present invention is used, heat generated inside areactor can be effectively controlled. Thus, the present invention canprovide a reaction system with a stable temperature gradient. Inaddition, even when the maximum temperature inside a catalyst bed islow, high reaction activity and stability can be provided. Therefore,the catalyst system of the present invention can improve the efficiencyof oxidative dehydrogenation.

1. A catalyst system for oxidative dehydrogenation, wherein a reactor isfilled with a catalyst for oxidative dehydrogenation in an n-layerstructure (n being an integer of 2 or more), wherein the catalyst isdiluted and the reactor is filled with the diluted catalyst so that eachlayer of the n-layer structure satisfies Equations 1 and 2 below:X wt %+Y wt %+Z wt %=100 wt %,  [Equation 1] wherein X represents anamount of AB₂O₄ and is 3 to 30, wherein A is one or more selected fromthe group consisting of copper (Cu), radium (Ra), barium (Ba), strontium(Sr), calcium (Ca), beryllium (Be), zinc (Zn), magnesium (Mg), manganese(Mn), cerium (Ce), zirconium (Zr), lanthanum (La), and cobalt (Co) and Bis iron (Fe); Y is an amount of a porous support and is 20 to 97; and Zis an amount of one or more dilution fillers selected from alumina,silica, silicon carbide, zirconia, titania, and cordierite and is 0 to77;X _(n) >X _(n−1),  [Equation 2] wherein, with respect to a direction inwhich reactants are fed into the reactor, X_(n) represents X for an n-thlayer, and X_(n−1) represents X for an (n−1)th layer.
 2. The catalystsystem according to claim 1, wherein n is an integer of 2 to
 8. 3. Thecatalyst system according to claim 1, wherein the catalyst systemsatisfies Equation 3 below:(X _(n) −X _(n−1))≥2,  [Equation 3] wherein X_(n) represents X for ann-th layer, and X_(n−1) represents X for an (n−1)th layer.
 4. Thecatalyst system according to claim 1, wherein at least one of the nlayers has a Z value greater than
 0. 5. The catalyst system according toclaim 1, wherein, when at least one layer has a Z value other than 0,the catalyst system satisfies Equation 4 below:(Y _(n) −Y _(n−1))≥15,  [Equation 4] wherein Y_(n) represents Y for then-th layer, and Y_(n−1) represents Y for the (n−1)th layer.
 6. Thecatalyst system according to claim 1, wherein the catalyst systemsatisfies Equation 5 below:(Z _(n−1) −Z _(n))≥20,  [Equation 5] wherein Z_(n) represents Z for then-th layer, and Z_(n−1) represents Z for the (n−1)th layer.
 7. Thecatalyst system according to claim 1, wherein AB₂O₄ is a coatingcatalyst coated on the porous support.
 8. The catalyst system accordingto claim 7, wherein the coating catalyst is a binder-free catalyst. 9.The catalyst system according to claim 1, wherein AB₂O₄ is a zincferrite, wherein A is Zn and B is Fe.
 10. The catalyst system accordingto claim 1, wherein the porous support is one or more selected from thegroup consisting of alumina, silica, titania, zirconia, silicon carbide,and cordierite.
 11. The catalyst system according to claim 1, whereinthe porous support has an average pore size of 50 to 200 μm.
 12. Thecatalyst system according to claim 1, wherein the porous support has apacking density of 0.8 to 1.5 kg/m³.
 13. A catalyst system for oxidativedehydrogenation, wherein a reactor is filled with a catalyst foroxidative dehydrogenation, wherein the catalyst is diluted and thereactor is filled with the diluted catalyst so as to satisfy Equation 6below:X wt %+Y wt %+Z wt %=100 wt %,  [Equation 6] wherein X is an amount ofAB₂O₄ and is 5 to 25, wherein A is one or more selected from the groupconsisting of copper (Cu), radium (Ra), barium (Ba), strontium (Sr),calcium (Ca), beryllium (Be), zinc (Zn), magnesium (Mg), manganese (Mn),cerium (Ce), zirconium (Zr), lanthanum (La), and cobalt (Co) and B isiron (Fe); Y is an amount of a porous support and is 25 to 85; and Z isan amount of one or more dilution fillers selected from alumina, silica,silicon carbide, zirconia, titania, and cordierite and is 10 to
 70. 14.A catalyst system for oxidative dehydrogenation, wherein a reactor isfilled with a catalyst for oxidative dehydrogenation in an n-layerstructure (n being an integer of 2 or more), wherein the catalyst isdiluted and the reactor is filled with the diluted catalyst so that eachlayer of the n-layer structure satisfies Equations 1 and 2 below:X wt %+Y wt %+Z wt %=100 wt %,  [Equation 1] wherein X represents anamount of AB₂O₄ and is 3 to 30, wherein A is one or more selected fromthe group consisting of copper (Cu), radium (Ra), barium (Ba), strontium(Sr), calcium (Ca), beryllium (Be), zinc (Zn), magnesium (Mg), manganese(Mn), cerium (Ce), zirconium (Zr), lanthanum (La), and cobalt (Co) and Bis iron (Fe); Y is an amount of a porous support having a packingdensity of 0.8 to 1.5 kg/m³ and is 20 to 97; and Z is an amount of oneor more dilution fillers selected from alumina, silica, silicon carbide,zirconia, titania, and cordierite and is 0 to 77;X _(n) >X _(n−1),  [Equation 2] wherein, with respect to a direction inwhich reactants are fed into the reactor, X_(n) represents X for an n-thlayer, and X_(n−1) represents X for an (n−1)th layer.
 15. A reactor forpreparing butadiene, comprising the catalyst system for oxidativedehydrogenation of claim
 1. 16. A method of preparing 1,3-butadiene,comprising: performing oxidative dehydrogenation using the reactoraccording to claim 15, wherein the oxidative dehydrogenation isperformed while continuously passing reactants containing a C4 compoundcomprising normal butene through a catalyst bed of the reactor.